The stability as well as the electrical properties of both unirradiated and γ-irradiated poly(vinyl alcohol)-PVA films doped with MnSO4.H2O at a definite concentration of 15% have been studied. The dielectric loss tangent tan δ, electrical conductivity σ and dielectric constant ε’ in the frequency range 100 Hz-20 KHz were measured at different temperatures. It has been demonstrated that the suitable mechanism of conduction is the correlated barrier hopping model. The exponent S according to the relation σ(ω)=A(ω)s was estimated and found to be less than unity and decreased with increasing the temperature Furthermore a nonlinearly of log σ against log f was observed at log f in the range (3.7-4.3) for doses ≥100 kGy at the temperatures of 333 and 343 k.
(2000). AC-Conductivity and Dielectric Properties of γ-Irradiated PVA Films Doped With Mn2+ Ions. Egyptian Journal of Solids, 23(2), 277-286. doi: 10.21608/ejs.2000.151737
MLA
. "AC-Conductivity and Dielectric Properties of γ-Irradiated PVA Films Doped With Mn2+ Ions". Egyptian Journal of Solids, 23, 2, 2000, 277-286. doi: 10.21608/ejs.2000.151737
HARVARD
(2000). 'AC-Conductivity and Dielectric Properties of γ-Irradiated PVA Films Doped With Mn2+ Ions', Egyptian Journal of Solids, 23(2), pp. 277-286. doi: 10.21608/ejs.2000.151737
VANCOUVER
AC-Conductivity and Dielectric Properties of γ-Irradiated PVA Films Doped With Mn2+ Ions. Egyptian Journal of Solids, 2000; 23(2): 277-286. doi: 10.21608/ejs.2000.151737